  • 高張力鋼の硬化熱影響部の切欠靱性:第2報再現熱サイクル試験

    寺沢 一雄 , 大谷 , 寺井 清 , 山田 桑太郎 , 酒戸 恒男

    The heat affected zones (HAZ) of three kinds of high tensile steels were reproduced with a synthetic thermal cycle apparatus, and their notch toughness was evaluated by fracture stress curve test and …

    造船協會論文集 1967(122), 157-173, 1967

    J-STAGE

  • 機械的応力除去が低荷重破壊に及ぼす影響の機構

    寺沢 一雄 , 大谷 , 上田 幸雄

    An investigation was performed into the effect of mechanical stress relieving on low load fracture of welded wide plate, reported by Prof. H. Kihara and his research group, and the analysis of the eff …

    造船協會論文集 1967(121), 213-224, 1967

    J-STAGE

  • 高張力鋼の硬化熱影響部の切欠靱性:第1報 ビード溶接試験

    寺沢 一雄 , 大谷 , 寺井 清 , 山田 桑太郎 , 酒戸 恒男

    Experiments were made to investigate the notch toughness of bead welded high tension steels, WT 50, WT 60 and WT 80. Kinzel bend test and Double Blow impact test were performed to make clear the chara …

    造船協會論文集 1967(121), 198-212, 1967

    J-STAGE

  • 溶接構造用鋼の切欠靱性の研究 (第3報):各種溶着鋼の切欠靱性について

    寺沢 一雄 , 大谷 , 寺井 清 , 金谷 文善

    Investigations were previously performed about the effect of high temperature prestraining on the notch toughness and the characteristics of fracture stress curves of various structural steels.<BR& …

    造船協會論文集 1964(116), 105-114, 1964

    J-STAGE

  • 溶着鋼の遷移温度

    大谷 , 岡田 寛

    By varying the coating composition of electrodes, the properties of deposited metals were changed in series with regard to their elements and degree of deoxidation. Their ordinary mechanical propertie …

    溶接学会誌 23(5-6), 104-110, 1954

    J-STAGE

  • 衝撃試験に関する一考察(第1報)

    大谷

    Series of double blow impact test were performed on V-notched Charpy specimens at temperatures, -50°C to 70°C. The depths of cracks created by first light blows. were detected by dripping etching solu …

    溶接学会誌 23(11-12), 250-256, 1954

    J-STAGE

  • 熔接が鋼材の遷移温度に及ぼす影響について(第4報)

    大谷 , 太田 省三郎

    A longitudinal bead was laid on the surface of kahn tear test piece to investigate the effect of manual arc welding on the notch sensitivity of structural mild steel plates.<BR>The saw cut was l …

    溶接学会誌 23(1-2), 35-40, 1954

    J-STAGE

  • 熔接が鋼材の切欠脆性に及ぼす影響について(第1報)

    大谷 , 太田 省三郎

    Welded tear test piece of Kahn type was proposed to investigate the effect of manual arc welding on the notch sensitivity of structural mild steel plates, 11 charges of rimmed and killed ones produced …

    溶接学会誌 22(8), 266-274, 1953

    J-STAGE

  • 熔接が鋼材の切缺脆性に及ぼす影響について(第3報)

    大谷 , 太田 省三郎

    Notched bead bend specimen of Lehigh type was used to evaluate the influence of welding on the notch sensitivity of structural mild steels. The test pieces werc arc welded manually and compared with t …

    溶接学会誌 22(10-12), 359-367, 1953

    J-STAGE

  • 熔接棒被覆剤と使用性能の関係について

    大谷

    Some experiments upon coating materials were made to improve usability characteristics of an ilmenite type slag shielded electrode having excellent mechanical strengths. The test results showed that f …

    溶接学会誌 18(5), 80-88, 1949

    J-STAGE

  • 熔接棒の亀裂性試験

    大谷 , 藤原 典男

    本論文に於ては構 鋼用電氣熔接棒の龜裂性を試驗する2種の、方法が提案されて居る。試驗片は夫々第1圖及び第4圖に示す如きものである。第1法は隅肉熔接による試驗てあり第2 は固定V型接手熔接による試驗であつて、兩試驗結果の間には相當の閣聯が存する。筆者等の経験によれば之等試驗に合格した熔接棒は現場熔接工事に使用して龜裂發生の はなかつた。

    溶接学会誌 16(5), 239-244, 1947

    J-STAGE

  • 圓濤形殻熔接歪の研究

    大谷

    溶接学会誌 16(2), 173-188, 1947

    J-STAGE

  • 平板熔接歪の研究

    大谷

    平板V型衝合接手を多層盛熔接すれば板の繼析く歪を生ずると同時に熔接綿の縱曲りを伴ふ歪をも生ずることは既に指摘されて居る所であるが、後者の生因に關してはまだ定説がない樣である。筆者は本論文に於て板内の歪エネルギを考察しエネルギ法を利用して理論的に該歪の近似値を計算した。此の際多層盛熔接の結果として接手部佐板厚方向に布し板に繼析を生ぜしめ様とする應力に基く歪エネルギ値(V<SUB>3< …

    溶接学会誌 16(10), 347-360, 1947