- Effect of Heat Treatment on Microstructure and Mechanical Properties of New Titanium Alloys for Surgical Implantation
- セイタイヨウ シン Ti ゴウキン ノ ソシキ ト リキガク トクセイ ニ オ
この論文をさがす
抄録
Ti-15 mass%Zr-4%Nb-4%Ta-0.2%Pd and Ti-15%Sn-4%Nb-2%Ta-0.2%Pd alloys not containing harmful V and Al for surgical implantation in response to recent concerns about the long term safety of Ti-6%Al-4%V ELI (Extra low interstitial, ASTM specified for surgical implantation) were cast by plasma electron beam melting. The effect of heat treating on room temperature strength was investigated by aging treatment after solution treatment. The alloys were forged in their α and α+β regions, and then solution-treated at 953∼1173 K for 3.6 ks. Vickers hardness in the range below β transition temperature increases with increasing solution treating temperature and change of Vickers hardness in the range over its temperature is small. Optimized solution treatment conditions are 1038 K-3.6 ks for Ti-Zr alloy and 1098 K-3.6 ks for Ti-Sn alloy containing 15∼20 vol% primary α phase. After solution treatment under the optimized condition aging treatment was done at 623∼873 K for 600 s∼36 ks. Vickers hardness in aging below 723 K increases with increasing aging temperature and aging time. Optimized aging conditions for Ti-Zr and Ti-Sn alloys were at 673 K for 36 ks and at 723 K for 36 ks, respectively. The room temperature strengths of those alloys are superior to those of Ti-6%Al-4%V ELI for medical implants. It is revealed by transmission electron macroscopic observation that fine α phase precipitates in the α′ martensitic matrix are responsible for the age hardening.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 59 (1), 108-115, 1995
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206491560192
-
- NII論文ID
- 10001668947
- 10003508926
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3601780
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可