Effect of SiO2-SrCO3 Addition on Magnetic Properties of Anisotropic Ba-ferrite(Ferrite Magnets Having Equal Shrinkage Ratio in A-axis and C-axis).

DOI Web Site 1 Citations 12 References

Bibliographic Information

Other Title
  • 磁性材料の化学　異方性Ｂａフェライトに対するＳｉＯ２‐ＳｒＣＯ３複合添加の影響（等縮率フェライト磁石）
  • イホウセイ Ba フェライト ニ タイスル SiO2 SrCO3 フクゴウ テ

Search this article

Abstract

Today, Sr-ferrite and Ba-ferrite with hexagonal structure are widely used as permanent magnets. However, Ba-ferrite is considered to be unsuitable for high performance magnets compared with Srferrite because of its lower K1 value. In this study, submicron-sized Ba-ferrite powders were prepared to achieve higher corecivity. On the other hand, addition of SiO2 and CaCO3 (or CaO) is usually carried out to get high density and inhibit grain-growth during sintering. Without difficulty, it is predicted that Sr and Ba can be substituted for Ca, because they have similar characters. Therefore, in this study, addition of alkaline-earth elements and silica was investigated systematically. As a result, by addition of Si02-SrCO3 in Ba-ferrite, high performance Ba-ferrite magnets (Br=4.3kG, HcJ=3.6kOe) were obtained. At the same time, we discovered that they have equal shrinkage ratio in a-axis and c-axis. These unique results were due to the inhibition of grain-growth along a-axis. Furthermore, Ba segregation was found at grain boundaries besides Si and Sr by TEM-EDS analysis.

Journal

Citations (1)*help

See more

References(12)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top