Preparation of Molybdenum Single Crystal with a Desired Orientation by Means of Zone Annealing.
-
- Kamihira Kazushige
- National Research Institute for Metals
-
- Honda Kinichi
- National Research Institute for Metals
-
- Fujii Tadayuki
- National Research Institute for Metals
Bibliographic Information
- Other Title
-
- 帯域焼鈍法による所望方位を有するMo単結晶の作製
- タイイキ ヤキナマシホウ ニヨル ショモウ ホウイ オ ユウスル Mo タンケ
Search this article
Abstract
A new technique for preparation of molybdenum single crystal with a desired orientation has been proposed. The technique was performed as follows; first, a specimen with a comb shape was mechanically fabricated from hot-rolled sheet with various rolling procedures and reductions. Then the edge of specimen with a comb shape was locally heated by the optical-beam image furnace in order to make some secondary recrystallized grains with various orientations. After the secondary recrystallized grains were mechanically eliminated except for a secondary grain having a desired orientation, the specimen was zone-annealed at 2000-2200°C at the zone-speed of 5 mm/ hr to grow the secondary grain. Consequently, molybdenum single crystal with a desired crystallographic orientation can easily be produced.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 44 (8), 770-774, 1997
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681285093760
-
- NII Article ID
- 10002014433
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4275743
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed