アルミナ複合植物研磨材によるバレル研磨　第２報　アルミナ系複合セラミックスの研磨

• 竹内 茂夫

  長野県工業試験場

書誌事項

タイトル別名

• Barrel Polishing with Alumina-Composite Botanical Abrasives. 2. Polishing of Alumina-Based Composite Ceramics.
• アルミナ フクゴウ ショクブツ ケンマザイ ニヨル バレル ケンマ ダイ 2ホ
• 2. Polishing of Alumina-Based Composite Ceramics
• アルミナ系複合セラミックスの研磨

抄録

Alumina-composite botanical abrasives were prepared by using aliphatic acid, wax, etc. to make a walunt shell composite with alumina powder. A barrel polishing apparatus was used to perform polishing experiments on various composite ceramics of the Al₂O₃-Y₂O₃-ZrO₂-MgO family (Family I, with high hardness and tenacity) and the Al₂O₃-Y₂O₃-MgO family (Family II, with high porosity). The alumina-composite botanical abrasives were found (1) to be capable of gradually increasing the polished amount with polishing time for all ceramics, with resulting improvement of surface roughness, (2) to be effective for smoothing surfaces of Family I composite ceramics, though with low processing efficiency, and (3) to exhibit high polishing speeds for Family II composite ceramics, though with high roughness of the finished surface.

収録刊行物

• 表面技術

  表面技術 48 (7), 740-745, 1997

  一般社団法人 表面技術協会

キーワード

• Walnut Shell
• Alumina-Composite Botanical Abrasives
• Al₂O₃-Y₂O₃-ZrO₂-MgO Composite Ceramics
• Al₂O₃-Y₂O₃-MgO Composite Ceramics
• Barrel Polishing
• Surface Roughness
• Polishing Speed

詳細情報

• CRID: 1390001204114088576
• NII論文ID: 10002259523
• NII書誌ID: AN1005202X
• DOI: 10.4139/sfj.48.740
• ISSN: 18843409
• ISSN: 09151869
• NDL書誌ID: 4248983
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4248983
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可