On Magnetic Shielding Effectiveness of Porous, Corrosion-Resistant PM Magnetic Alloys.
-
- Kusaka Katsushi
- Daido Institute of Technology
-
- Komura Takahiro
- Daido Institute of Technology
-
- Kondo Tetsuya
- Daido Steel Co., Ltd.
Bibliographic Information
- Other Title
-
- 磁石・磁性材料の化学 II 多孔質,耐食性PM磁性材料の磁気シールド効果について
- タコウシツ タイショクセイ PM ジセイ ザイリョウ ノ ジキ シールド コウカ ニ ツイテ
Search this article
Abstract
The objective of this study is mainly to evaluate PM ferritic stainless steel as magnetic shielding plate, comparing with PM PB-permalloy. In this case, PM plate thickness and sintering temperature (1173-1623K) were employed as parameters to optimize DC/AC (≤10kHz) magnetic shielding effect of materials, including magnetic measuring apparatus arrangement.<BR>The results obtained in these conditions were summarized as follows:<BR>(1) DC magnetic field is allowed to attenuate to a saturate level by using PM plate with 4mm thick which is sintered at 1273K at the lowest, while the saturate value decreases with the distance (r) from a magnetic source.<BR>(2) AC magnetic field also is allowed to attenuate to a saturate level by using PM plate with 4mm thick which is sintered at 1373K at the lowest, although the saturate value differentiates between the frequencies of 1 and 10 kHz.<BR>(3) Magnetic attenuation (dB) is fairly enhanced when a covering of the high-μ permalloy sheet is put on the periphery of PM plate in DC and 1 kHz range, although it is not effective in higher frequency range.<BR>(4) Bend strength of PM plate shows a higher value by being sintered at higher temperature (ex.-200MPa at 1373K), untouched by the direct influence of material itself.<BR>(5) PM ferritic stainless steel proved to have almost the same magnetic shielding effect as PM PB-permalloy, when sintered at 1373K or higher, and consequently, to be used as porous, corrosion-resistant magnetic shielding alloy.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 46 (2), 156-162, 1999
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681285403904
-
- NII Article ID
- 10002261836
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4655536
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed