Thermodynamics of the MnO-SiO2-TiO2 System at 1673 K.

• Ito Maki

  Department of Metallurgy, The University of Tokyo

• Morita Kazuki

  Department of Metallurgy, The University of Tokyo

• Sano Nobuo

  Department of Metallurgy, The University of Tokyo

抄録

The isothermal phase relations for the MnO-SiO₂-TiO₂ system have been investigated at 1673 K by a chemical equilibration technique. Iso-activity curves for MnO are drawn from the experimental results of the activities as well as those for SiO₂ and TiO₂ calculated by Schuhmann's tangent intercept procedure.¹⁾ Iso-activity curves are nearly parallel to the saturation lines for the respective components. In this system, the interaction between MnO and SiO₂ is the strongest of all.<br> The sulfide capacity mostly depends on MnO content in this ternary system. It slightly increases when SiO₂ is replaced by TiO₂ at a constant (MnO+MnS) content by molar basis, whereas γ_MnS considerably decreases.

収録刊行物

• ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ

  ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ 37 (9), 839-843, 1997

  一般社団法人 日本鉄鋼協会

キーワード

• phase equilibria
• solubility
• iso-activity curve
• oxide metallurgy
• MnO-SiO₂
• MnO-TiO₂
• MnO-SiO₂-TiO₂
• sulfide capacity

詳細情報

• CRID: 1390282681431021696
• NII論文ID: 10002456846
• NII書誌ID: AA10680712
• DOI: 10.2355/isijinternational.37.839
• ISSN: 13475460
• ISSN: 09151559
• ISSN: http://id.crossref.org/issn/09151559
• Web Site: http://www.jstage.jst.go.jp/article/isijinternational1989/37/9/37_9_839/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可