OCCプロセスによる Cu-Al-Ni 形状記憶合金線の連続鋳造

• 本保 元次郎

  千葉工業大学金属工学科　工博

• 金子 道紀

  千葉工業大学大学院〔現　（株）オプトニクス精密〕

• 藤原 靖幸

  千葉工業大学金属工学科

• 早田 博

  トロント大学　金属・材料工学科　工博

書誌事項

タイトル別名

• Continuous Casting of Shape Memory Cu-Al-Ni Alloy Wires by OCC Process
• OCCプロセスによるCu-AI-Ni形状記憶合金線の連続鋳造
• OCC プロセスニヨルCu-AI-Ni ケイジョウ キオク ゴウキンセン ノ

抄録

  The possibility of applying the Ohno continuous casting (OCC) process for fabricating Cu-based shape memory alloy wires was examined using Cu-14.1 mass % Al-4.2 mass % Ni alloy. Most of the cast wires, 2mm in diameter, were found to have unidirectional structures with a matrix phase of β₁ in which fine γ₂ particles were dispersed. It was found that at a lower casting speed range (0.8∼1.5 mm/ s), the cast wires showed shape memory effects arising from stress-induced martensitic transformations. At higher casting speeds (1.8∼2.5 mm/s), the cast wires produced exhibited super elasticity at room temperature. In addition, the fatigue failure of the cast wires (casting speed : 2.5 mm/s) occurred after 6500 of cycles of bending.

収録刊行物

• 鋳造工学

  鋳造工学 70 (9), 635-640, 1998

  公益社団法人 日本鋳造工学会

キーワード

• Cu-Al-Ni Alloy
• continuous casting
• unidirectional solidified structure
• shape memory effect

詳細情報

• CRID: 1390001206506190848
• NII論文ID: 10002554162
• NII書誌ID: AN10514770
• DOI: 10.11279/jfes.70.635
• ISSN: 21855374
• ISSN: 13420429
• NDL書誌ID: 4564963
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4564963
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可