Electrochemical investigation on pitting corrosion generation of aluminum alloy in the solution containing SO42- ion.
-
- KURODA Shuu
- Technical development center, Mitsubishi Aluminum Co., Ltd.
-
- TOHMA Ken
- Technical development center, Mitsubishi Aluminum Co., Ltd.
Bibliographic Information
- Other Title
-
- SO4`2-´イオンを含んだ溶液中でのアルミニウム合金の孔食発生に関する電気化学的検討
- SO42-イオンを含んだ溶液中でのアルミニウム合金の孔食発生に関する電気化学的検討
- SO42- イオン オ フクンダ ヨウエキチュウ デ ノ アルミニウム ゴウキ
Search this article
Abstract
To investigate the effect of SO42- ion on pitting corrosion behavior of aluminum and aluminum alloy brazing sheets immersion corrosion test and electrochemical measurements were carried out in the solution of lower chloride concentration containing SO42- ion. As the SO42- ion reduced the anodic and cathodic reaction rate, the pitting corrosion resistance of aluminum increased. The pitting corrosion occurred even in solution containing SO42- when the cathodic reaction was high enough. In that case the pitting corrosion rate was much higher than that in the SO42- ion free solution. Higher pitting corrosion rate induced by SO42- ion was due to the lower pitting corrosion density which was closely related with the thicker oxide film formed on aluminum surface. The probability of pitting corrosion was estimated with the relation between Ecorr and Erep value in anodic polarization measurement in the solution.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 48 (6), 282-287, 1998
The Japan Institute of Light Metals
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681314007808
-
- NII Article ID
- 10002664848
- 10004011039
-
- NII Book ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1cXkt1Wlurc%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 4512223
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed