X-Ray Diffraction and Dielectric Measurements of PbZrO3 under High Pressures.
-
- Kobayashi Y.
- Research Center for Materials Science at Extreme Conditions, Osaka University
-
- Endo S.
- Research Center for Materials Science at Extreme Conditions, Osaka University
-
- Deguchi K.
- Shizuoka Institute of Science and Technology
-
- Ming L. C.
- Hawaii Institute of Geophysics and Planetology, University of Hawaii at Manoa
-
- Shieh S. R.
- Hawaii Institute of Geophysics and Planetology, University of Hawaii at Manoa
-
- Ashida T.
- Department of Industrial Chemistry, Kinki University
-
- Shimomura O.
- National Laboratory for High Energy Physics
-
- Kikegawa T.
- National Laboratory for High Energy Physics
-
- Fujishita H.
- Department of Physics, Kanazawa University
Bibliographic Information
- Other Title
-
- X-Ray Diffraction and Dielectric Measurement of PbZrO3 under High Pressures
- X-Ray Diffraction and Dielectric Measur
Search this article
Abstract
X-ray diffraction, dielectric constant measurement, and microscopic observation were carried out on antiferroelectric PbZrO3 under high pressures up to78, 22, and 48 GPa, respectively, at room temperature. By x-ray diffraction analyses, it was clearly recongnized that an orthorhombic ambient-pressure phase transforms to a monoclinic phase at around 37 GPa, and then again to a slightly different monoclinic phase above 75GPa. A large anomaly in the dielectric constant was observed at around 19 GPa, which strongly suggests the appearance of ferroelectricity in PbZrO3 at high pressure. Optical observation showed that the color changes from pale yellow into thin red at around 19 GPa and then further to black at around 37 GPa. The former change is associated with the dielectric anomaly and the latter with the phase transition to a monoclinic phase discovered by x-ray diffraction.
Journal
-
- The Review of High Pressure Science and Technology
-
The Review of High Pressure Science and Technology 7 310-312, 1998
The Japan Society of High Pressure Science and Technology
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204382322304
-
- NII Article ID
- 10002689900
-
- NII Book ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL BIB ID
- 4493913
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed