粒子強化型P/M Ti-6Al-2Sn-4Zr-2Mo/TiB複合材料の製造と特性評価

DOI Web Site Web Site 被引用文献1件 参考文献19件

書誌事項

タイトル別名
  • Synthesis and Property Evaluation of P/M Ti-6Al-2Sn-4Zr-2Mo/TiB Particulate Composites
  • リュウシ キョウカガタ PM Ti 6Al 2Sn 4Zr 2Mo TiB フ

この論文をさがす

抄録

Conventional titanium alloys such as Ti-6Al-4V show lower stiffness, poorer abration-related properties and poorer high temperature properties than nickel-based alloys. In order to overcome these drawbacks, an attempt was made to produce titanium-based particulate composites using the blended elemental powder metallurgy method. Firstly, the effect of titanium powder size on the sintered density and how to disperse the reinforcing ceramic particulates uniformly in the matrix were investigated in detail to optimize processing conditions. It was shown that the size of titanium powder needs to be smaller than 45μm (-325mesh) to raise the sintered density to a critical value of 95%. The uniform distribution of the particulates was accomplished by a forced mixing technique with a mechanofusion apparatus. Secondly, Ti-6Al-2Sn-4Zr-2Mo/TiB composites were produced using the above processing conditions. The composites showed superior tensile properties, Young's modulus and high cycle fatigue strength compared with those for the matrix alloy. For example, high cycle fatigue strength at 107 cycles was increased to 490MPa from 333MPa for the matrix alloy by the dispersion of 10% TiB. The tensile and Young's modulus data were compared with those predicted by the existing models, and three main factors such as the increase in tensile strength, increase in Young's modulus and matrix microstructure refinement were found to contribute to the increase in high cycle fatigue strength.

収録刊行物

  • 鉄と鋼

    鉄と鋼 83 (12), 821-826, 1997

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

参考文献 (19)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ