- Brittleness of Sendust
- センダスト ノ ゼイセイ
この論文をさがす
抄録
The brittleness of Sendust with the nominal composition of 9.6% silicon, 5.4% aluminum and the balance of iron has been studied experimentally. By high thermal stress due to temperature gradient in the crystal, cleavage cracks along {001} plane or grain boundary cracks are easily introduced during either solidification after casting or subsequent heat treatments. The {001} cleavage cracks are also formed under applied external stress. Fracture stress of hot rolled Sendust examined by bending tests is higher than that of cast one, indicating the removal of internal defects by hot rolling. The single crystal which was prepared by zone-melting, and therefore, less-stressed thermally can be bent plastically even at room temperature, showing a lack of internal defects acting as the origin of cracking.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 47 (4), 336-342, 1983
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681461835520
-
- NII論文ID
- 40002875573
- 130007338457
- 10003381704
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2589920
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可