AC4CHアルミニウム合金試験片の組織と強さに及ぼす鋳造条件の影響 Effect of casting conditions on the strength of the AC4CH aluminum casting alloy specimen

この論文にアクセスする

この論文をさがす

著者

抄録

Effect of casting condition, especially of cooling rates, on the microstructures and mechanical properties of the AC4CH aluminum casting alloy has been investigated and the following results were obtained. Clear effect of the cooling rate on the dendritic structures was observed and reasonable linear relation between log DAS (dendrite arm spacing) and log R (cooling rate) was ascertained. In case of copper mold application, higher cooling rate dependence was obtained for the growth of the dendrite as compared to that of iron mold. Increase of the cooling rate resulted in an effective refining of the eutectic silicon phase, while a weak influence was observed on the spheroidization coefficient of the eutectic silicon. Effect of the cooling rate on the tensile strength was remarkable under the conditions of under-aging and over-aging. Higher values of the absorbed energy in the Charpy impact fracture were obtained by applications of the copper mold. Increase of the cooling rate raised magnesium concentration in the matrix. Above all, higher magnesium concentrations were certainly obtained for the copper mold applications as compared to those of iron mold.

収録刊行物

  • 軽金属

    軽金属 46(8), 365-370, 1996-08-30

    The Japan Institute of Light Metals

参考文献:  11件中 1-11件 を表示

被引用文献:  2件中 1-2件 を表示

各種コード

  • NII論文ID(NAID)
    10003794270
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    4021305
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ