Mg–Al系合金の半溶融成形加工時の流動性

• 大西 智

  長岡技術科学大学大学院

• 平田 幸四郎

  長岡技術科学大学大学院

• 鎌士 重晴

  長岡技術科学大学

• 小島 陽

  長岡技術科学大学

書誌事項

タイトル別名

• Fluidity during semi-solid forming of Mg–Al alloys
• Mg Alケイ ゴウキン ノ ハン ヨウユウ セイケイ カコウジ ノ リュウド
• Fluidity during semi-solid forming of Mg–Al alloys

抄録

The fluidity of Mg–Al specimen has been investigated in order to establish semi-solid press-forming technology. The fluidity of strain-introduced specimen is much better than that of non-strained specimen leading to the microstructure with uniformly-distributed spherical particles. Fluidity during semi-solid press-forming of strain-introduced bulk increases with increase in the die temperature. But when injection speed is too high, porosity is easily generated because air bubbles are trapped into the specimen due to turbulent flow of semi-solid specimen. Too large particles gather in step section of die, resulting in the segregation of liquid phase.

収録刊行物

• 軽金属

  軽金属 46 (12), 644-649, 1996

  一般社団法人 軽金属学会

キーワード

• semi-solid press-forming
• magnesium alloy
• fluidity
• microstructure
• strain-introduced bulk

詳細情報

• CRID: 1390001206338073984
• NII論文ID: 10003794726
• NII書誌ID: AN00069773
• DOI: 10.2464/jilm.46.644
• COI: 1:CAS:528:DyaK2sXovVanuw%3D%3D
• ISSN: 18808018
• ISSN: 04515994
• NDL書誌ID: 4118752
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4118752
• Web Site: https://www.jstage.jst.go.jp/article/jilm/46/12/46_12_644/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可