- Elevated-temperature strength of Al-7.8mass%V-4mass%Fe alloy containing icosahedral phase produced by extrusion of atomized powder.
- 準結晶を含むガス噴霧Al-7.8%V-4%Fe合金粉末の押出成形と耐熱強度
- ジュンケッショウ オ フクム ガス フンム Al 7.8パーセント V 4パー
この論文をさがす
抄録
The bulk material with a size of about φ8 mm × 300 mm was produced by extrusion of gas atomized Al–7.8 mass%V–4 mass%Fe alloy powder at 623, 673 and 723 K. The gas atomized powder consists of icosahedral, fcc–Al and Al11V phases and has a spherical shape with an average diameter of about 31 μm. The bulk material extruded at 623 K consists of icosahedral and Al phases and has a high packing density of approximately 100%. The ultimate tensile strength (σUTS), plastic elongation (εP), Vickers hardness (HV) and Young's modulus (E) at room temperature are 585 MPa, 4.5%, 190 and 84.8 GPa, respectively. And then the σUTS, εP and HV at 573 K are 305 MPa, 5.0% and 90, respectively. The HV remains unchanged even after holding for 432 ks at 573 K. The coefficient of thermal expansion is 21.4 × 10−6K−1, which is smaller by 15% than that of the 7075–T6 alloy. The bulk materials extruded at 673 and 723 K also have the similar high elevated temperature strength of 291 and 277 MPa, respectively, at the temperature 573 K. The extruded bulk materials with high elevated-temperature strength are expected to develop as a new type of high strength material.
収録刊行物
-
- 軽金属
-
軽金属 47 (10), 539-544, 1997
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206337262592
-
- NII論文ID
- 10003381122
- 10003796003
- 10003905014
- 10003381292
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK2sXmvF2mtL0%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4324280
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可