一方向凝固したFe-C系合金の黒鉛片間隔に及ぼすいおうとけい素の効果 Effects of Sulfur and Silicon on Inter-Graphite Spacing in Unidirectionally Solidified Fe-C Alloy

この論文にアクセスする

この論文をさがす

著者

抄録

  The effects of sulfur and silicon on inter-graphite spacing <i>λ</i> in gray cast iron has been investigated by unidirectional solidification with Bridgman method. Sulfur content was varied from 0.004 to 0.108mass%, and silicon content was varied from 0.068 to 1.10mass%. The speed of crucible <i>V</i> was varied from 0.00015 to 0.01000cm/s. The temperature gradient at solid-liquid interface was 18∼21K/cm. The experimental equations of <i>λ</i>-<i>V</i> were obtained by using linear regression analysis. It was clarified that the transition from flake to undercooled graphite shifted differently according to sulfur and silicon content.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society

    鋳造工学 = Journal of Japan Foundry Engineering Society 69(4), 297-303, 1997-04

    公益社団法人 日本鋳造工学会

参考文献:  14件中 1-14件 を表示

  • <no title>

    CROKER

    Proc. Roy. Soc. 335, 15, 1973

    被引用文献1件

  • <no title>

    森田善一郎

    鉄と鋼 74, 1210, 1988

    被引用文献2件

  • <no title>

    JACKSON K. A.

    Trans. Met. Soc. AIME 236, 1129, 1966

    被引用文献3件

  • <no title>

    SAYAMA Y.

    J. Crystal Growth 22, 272, 1974

    被引用文献2件

  • <no title>

    OHIRA G.

    The Metallugy of Cast Iron 295, 1975

    被引用文献1件

  • <no title>

    NIESWAAG H.

    The Metallurgy of Cast Iron 327, 1975

    被引用文献2件

  • <no title>

    HILLERT M.

    The Solidification of Metals 204, 1967

    被引用文献1件

  • <no title>

    FREDRIKSON H.

    The Metallurgy of Cast Iron 277, 1975

    被引用文献1件

  • <no title>

    FREDRIKSON H.

    The Metallurgy of Cast Iron 315, 1975

    被引用文献1件

  • <no title>

    中江秀雄

    金属学会誌 58, 30, 1994

    被引用文献1件

  • <no title>

    坂本敏正

    鋳物 50, 549, 1978

    被引用文献1件

  • <no title>

    茨木正雄

    金属学会誌 31, 690, 1967

    被引用文献1件

  • <no title>

    岸武勝彦

    鋳物 53, 295, 1981

    被引用文献4件

  • <no title>

    MAGNIN P.

    Acta. Met. 35, 1119, 1987

    被引用文献1件

各種コード

  • NII論文ID(NAID)
    10003800126
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    4194330
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ