Mechanical Milling of Pure Ti and Pure Zr

• Liu X. D.

  Laboratory for Materials Science and Technology, Waseda University

• Nagumo M.

  Laboratory for Materials Science and Technology, Waseda University

• Umemoto M.

書誌事項

タイトル別名

• Mechanical Milling of Pure Ti and Pure

抄録

Pure elemental Ti and Zr powders are respectively subjected to mechanical milling. It is discovered that after milling for 100 h, amorphization occurs in Zr while only nanocrystallization is achieved in Ti. Further thermal analysis and electron microscope observations verify amorphization in the 100 h-milled Zr sample. The crystallization peak temperature of the 100 h-milled Zr sample is determined to be 875 K by using a differential scanning calorimeter at a heating rate of 40 K/min. The above experimental results are discussed.

収録刊行物

• Materials Transactions, JIM

  Materials Transactions, JIM 39 (4), 463-468, 1998

  社団法人 日本金属学会

キーワード

• mechanical milling
• titanium and zirconium
• amorphization
• nanocrystallization

詳細情報

• CRID: 1390282679224112128
• NII論文ID: 10003802401
• NII書誌ID: AA10699969
• DOI: 10.2320/matertrans1989.39.463
• COI: 1:CAS:528:DyaK1cXjs1yjsLY%3D
• ISSN: 2432471X
• ISSN: 09161821
• NDL書誌ID: 4483594
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4483594
• Web Site: https://www.jstage.jst.go.jp/article/matertrans1989/39/4/39_4_463/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可