Protium Absorption Properties of La–TM–Si (TM=Co, Ni) Ternary Intermetallic Compounds
-
- Kakuta Hirofumi
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Ogawa Toshiyuki
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Takamura Hitoshi
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Okada Masuo
- Department of Materials Science, Graduate School of Engineering, Tohoku University
書誌事項
- タイトル別名
-
- Protium Absorption Properties of La–TM–Si (TM=Co, Ni) Ternary Intermetallic Compounds
- Protium Absorption Properties of La-TM-
この論文をさがす
抄録
The protium-absorbing characteristics such as the amount of absorbing protium and the hydrogen reaction have been studied for the LaTMSi, LaTMSi2 and LaTM2Si2 (TM=Co, Ni) ternary intermetallic compounds. For these compounds, it is found from DSC measurements that only the LaCoSi and LaNiSi compounds show hydride reactions at elevated temperatures. The LaCoSi alloy has a disproportionation reaction at 457 K, whereas the LaNiSi alloy reversibly absorbs and desorbs protium near 425 K. The maximum absorbed amount of protium is 0.52 mass% for the LaNiSi alloy.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (7), 769-772, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679223653888
-
- NII論文ID
- 130003557065
- 10003803282
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1cXls1Gks7k%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4525775
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可