- Thermomechanical Behavior of Thermal-Stress Relief Type of Functionally Gradient Material Evaluated by Differential Temperature Heating Using H<SUB>2</SUB>/O<SUB>2</SUB> Combustion Flame
- 熱応力緩和型傾斜機能材料のH2/O2燃焼ガス加熱による遮熱,耐熱特性評価
- ネツ オウリョク カンワガタ ケイシャ キノウ ザイリョウ ノ H2 O2 ネ
この論文をさがす
抄録
The burner heating test for thermomechanical evaluation of functionally gradient material in a laboratory scale has been described. A temperature difference was given by heating the ceramic side with a burner frame and cooling the metal side with water flow. The damage at the specimen surface was monitored with a microscope. A vertical crack formation at the ceramic surface was observed during cooling cycle. The test temperature for the first crack formation was defined as a thermal barrier performance value for the test sample. It has been found that the crack formation temperature is almost constant for the various samples and heating conditions, which indicates strong dependency of the thermal barrier property on the material species. The crack formation mechanism was discussed on the basis of a thermal stress analysis using a finite element method.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 56 (4), 472-480, 1992
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681466634624
-
- NII論文ID
- 40002877369
- 130007340660
- 10004209574
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
-
- NDL書誌ID
- 3765471
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可