- Preparation of .BETA.-FeSi2 Utilizing the Combined Process of MA/SPS.
- MA SPS フクゴウ プロセス ニ ヨル ベータ FeSi2 ノ サクセイ
この論文をさがす
抄録
β-FeSi2 was successfully produced by making use of the combined process of mechanical alloying (MA) and spark plasma sintering (SPS). The MA was perforomed under the Ar gas atomsphere using mixed powders of pure iron and silicon having the mole fraction of 1: 2. The SPS process was performed at 1073 K with the heating rate of 1.33 K/s and the holding time was ranging from 0 to 15 ks. The combined process was quite effective for the production of β-FeSi2, where the minimum SPS time required was found to depend on the MA time. The shortest SPS holding time of Os was achieved for the powders mechanically alloyed for 72ks.<BR>The relative density of each sinter is around 90% (4.44g/cm3) to its ideal density, and especially the density of 97.4% was obtained for the sinter which was mechanically alloyed for 72ks, followed by the SPS treatment for 600s.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 47 (4), 369-374, 2000
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284428288
-
- NII論文ID
- 10005137536
- 10010465947
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD3cXjvVahs7g%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 5362738
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可