Synthesis of New(W,Mo)(C,N) Powder by Heating W-Mo Alloy Powder in CH4+NH3 Mixed Gas of Normal-Pressure.
-
- Tanaka Kazuhiko
- Institute of Industrial Science, The University of Tokyo
-
- Hayashi Koji
- Institute of Industrial Science, The University of Tokyo
この論文をさがす
抄録
The authors had already succeeded in synthesizing the powders of new tungsten and molybdenum mono-carbonitrides, i.e., W(C, N) and Mo(C, N), by the following two processes: (1) high-pressure process: heating of W+C and Mo+C mixed powder in N2 gas of 10-150 MPa at 1523-1773 K, and (2) normal-pressure process: heating of W and Mo powder in CH4+NH3 mixed gas of 0.1 MPa at 1373-1573 K. In this study, the synthesis of (W0.3Mo0.7) (C, N) was attempted by the latter normal-pressure process, i.e., by heating W-70at%Mo alloy+C mixed powder in NH3 gas (method I) and by heating the alloy powder in CH4+NH3 mixed gas (method II). It was found that (W0.3Mo0.7) (C, N) with nitrogen contents of 23-21 at% could be synthesized by method II at 1373-1573 K. The maximum nitrogen content was fairly larger than 5 at% of W(C, N) and 17 at% of Mo(C, N) synthesized by method II, and also larger than 16-21 at% of (W0.3Mo0.7)(C, N) synthesized by the high-pressure process at 10-150 MPa.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 47 (9), 946-950, 2000
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308135168
-
- NII論文ID
- 10005138515
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 5485928
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可