- Development of SmFe7Nx+.ALPHA.Fe Nanocomposite Magnets.
- フンタイ フンマツ ヤキン キョウカイ ギジュツ シンポショウ ジュショウ キネン コウエン SmFe7Nx アルファ Feケイ ビサイ フクゴウ ジシャク ノ カイハツ
この論文をさがす
抄録
Nano composite magnet material consisting of hard magnetic SmFe7Nx phase and soft magnetic α Fe phase were developed through a process of rapidly quenching method including heat treatment and nitrogenation. Well balanced magnetic performance were obtained for the alloys with the composition of (Sm8Zr3Fe85Co4)N15. The ranges of grain sizes are 20-40nm which are enough small to create exchange coupling interaction between soft and hard magnetic grains. The ratio of α Fe phases with higher magnetization are measured approximately 20% by TEM observation. TEM-EDX study revealed that SmFe7Nx phase have a composition of richer Sm ratio than that of 1-7stoichiometry. Magnetic properties of those powders are as follows: Br=0.97T, HcJ=752kJ/m, (BH)max=140kJ/m3. Bonded magnets have been fabricated with thermoelastic and thermoplastic resins.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 46 (6), 581-588, 1999
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308193536
-
- NII論文ID
- 10005139517
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1MXksFarsb0%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 4770176
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可