溶融塩・液体金属の混合体を利用したTiCl<SUB>4</SUB>の還元

DOI Web Site Web Site 被引用文献6件 参考文献16件

書誌事項

タイトル別名
  • Reduction of TiCl<SUB>4</SUB> in Molten Salt/Liquid Metal Mixtures
  • 溶融塩・液体金属の混合体を利用したTiCl4の還元
  • ヨウユウエン エキタイ キンゾク ノ コンゴウタイ オ リヨウ シタ TiCl4 ノ カンゲン
  • Reduction of TiCl4 in molten salt/liquid metal mixtures

この論文をさがす

抄録

With the purpose of developing a new process for titanium powder production, a fundamental investigation on TiCl4 reduction in a reaction medium consisting of a mixture of molten salt and metal magnesium at 973 K was carried out. By applying an electrochemical potential on a feed injection nozzle, clogging of the feed tube was prevented. This anodic polarization technique is shown to be useful for feeding TiCl4 directly into the reactive reaction medium. As an alternate method for TiCl4 feed into the medium, a well-type mixer was specially designed and fabricated, and conditions for effective mixing of molten salt and metal phases were investigated. A preliminary experiment using water and oil showed that even the gas phase can be involved in the reaction medium under high rotation speed mixing (>700 min−1). When TiCl4 gas was fed into the gas phase above the reaction medium, some part of the feed reacted with the medium and was reduced to titanium metal. However, a major portion of the feed was reduced on the metal wall of the reaction container. When solidified TiCl4 was charged into the medium mixed by the mixer, titanium deposit in powder and sponge form was obtained. The amount of titanium power was increased with increasing rotation speed of the mixer. The mixture of molten salt and liquid metal is shown to be useful as a reaction medium for titanium powder production, however, the titanium deposit was found to adhere to the reaction wall under certain conditions.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 64 (10), 940-947, 2000

    公益社団法人 日本金属学会

被引用文献 (6)*注記

もっと見る

参考文献 (16)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ