Fe-30%Cr合金の延性に及ぼす粒界窒化物の形態の影響

DOI Web Site Web Site 被引用文献9件 参考文献6件

書誌事項

タイトル別名
  • Effect of Morphology of Grain Boundary Nitride on the Ductility of Fe-30 mass%Cr Alloys
  • Fe 30パーセント Cr ゴウキン ノ エンセイ ニ オヨボス リュウカイ チッカブツ ノ ケイタイ ノ エイキョウ

この論文をさがす

抄録

Effects of morphology of grain boundary nitride on the ductility of Fe-30 mass%Cr alloys containing N from 0.004 to 0.13 mass% were investigated. Two kinds of heat treatments were adopted to obtain the morphologies of continuous grain boundary nitride and of discontinuous grain boundary nitride. Tensile tests were carried out at temperatures ranging from 4.2 K to room temperature. Ductility was evaluated by transition temperatures in reduction of area.<BR>The results obtained are summarized as follows:<BR>(1) Upper shelf in reduction of area of the specimen containing discontinuous grain boundary nitride is higher than that of the specimen containing continuous grain boundary nitride.<BR>(2) Transition temperature of the specimen containing discontinuous grain boundary nitride is lower than that of the specimen containing continuous grain boundary nitride.<BR>(3) The area rate of intergranular fracture surface which appears in cleavage fracture surface observed in the specimen containing discontinuous grain boundary nitride is smaller than that which appears in cleavage fracture surface observed in the specimen containing continuous grain boundary nitride. The area rate of intergranular fracture surface which appears in dimple fracture surface also shows similar observation result.<BR>(4) Initiation of microcracks for brittle fracture may be caused by decohesion at the interfaces between the matrix and grain boundary nitride.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 63 (9), 1137-1140, 1999

    公益社団法人 日本金属学会

被引用文献 (9)*注記

もっと見る

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ