ＣＶＤ法によりＴｉＢ２／ＴｉＮ二層被覆したＳＫＤ６１鋼の溶融Ａｌにおける耐浸食性

• 佐藤 忠夫

  室蘭工業大学工学部

• 堀米 毅

  室蘭工業大学工学部

• 上田 幹人

  北海道大学大学院工学研究科

書誌事項

タイトル別名

• Improvement of Corrosion Resistivity for a Melted Aluminum Alloy of SKD 61 Steel by a TiB2/TiN Bilayered Coating Formed by Chemical Vapor Deposition.
• CVDホウ ニ ヨリ TiB2 TiNニソウ ヒフク シタ SKD 61 コウ ノ ヨウユウ Al ニ オケル タイシンショクセイ

抄録

TiB₂ and TiN films were coated by chemical vapor deposition on SKD 61 steel to improve the corrosion resistivity of a diecasting machine in a melted aluminum alloy. The protectivity of the film in the melted aluminum alloy was examined by an immersion test at 900°C and a thermal cycle test between room temperature and 900°C. TiN film, which serves as a binder, greatly improves the adhesion of TiB₂ film on the steel substrate. The thermal cycle test indicated that the optimum thickness of TiB₂ and TiN layers is at 4 and 6μm, respectively. Compared to ion-nitrized steel, steel coated by TiB₂/TiN exhibits significantly higher degree of corrosion resistivity.

収録刊行物

• 表面技術

  表面技術 51 (6), 640-645, 2000

  一般社団法人 表面技術協会

キーワード

• TiB₂/TiN
• CVD Coating
• Corrosion Resistivity
• in Melted Aluminum

詳細情報

• CRID: 1390001204113586688
• NII論文ID: 10006249542
• NII書誌ID: AN1005202X
• DOI: 10.4139/sfj.51.640
• ISSN: 18843409
• ISSN: 09151869
• HANDLE: 2115/74942
• NDL書誌ID: 5374334
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I5374334
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • IRDB
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可