- Kushida Ayako
- Department of Materials Science and Engineering, Kyoto University
-
- Ikeda Teruyuki
- Department of Materials Science and Engineering, Kyoto University
-
- Numakura Hiroshi
- Department of Materials Science and Engineering, Kyoto University
-
- Koiwa Masahiro
- Department of Materials Science and Engineering, Kyoto University
書誌事項
- タイトル別名
-
- Thermodynamic Activity of Ga in Ni<SUB><B>3</B></SUB>Ga
この論文をさがす
抄録
Thermodynamic activity of Ga in the L12-ordered intermetallic phase Ni3Ga has been determined by measuring the electromotive force of a galvanic cell with zirconia solid-electrolyte, Ni–Ga, Ga_2O_3|ZrO_2 (+ Y_2O_3) | Ga, Ga_2O_3in the temperature range between 1050 and 1300 K for six compositions. The activity of Ga varies with composition most steeply at the stoichiometric composition (25 mol%Ga), the dependence being more pronounced at low temperatures. By applying a thermodynamic model based on the Bragg-Williams approximation (Ikeda et al.: Acta Mater. 46 (1998) 6605–6613), the effective pair interaction energy between Ni and Ga atoms has been determined to be 9.75±0.19 kJ/mol. The thermodynamic factor in chemical diffusion in the L12 phase has been derived from the composition dependence of the thermodynamic activity.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (3), 514-519, 2001
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222482560
-
- NII論文ID
- 10006547836
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXjtlSjtLc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 5729627
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可