Gas Nitriding of Magnesium--Titanium Alloys Fabricated by Bulk Mechanical Alloying
-
- Luangvaranunt Tachai
- Research Center for Advanced Science and Technology, University of Tokyo
-
- Visuttipitukul Patama
- Research Center for Advanced Science and Technology, University of Tokyo
-
- Kondoh Katsuyoshi
- Research Center for Advanced Science and Technology, University of Tokyo
-
- Kuwahara Hideyuki
- Research Institute for Applied Sciences
-
- Aizawa Tatsuhiko
- Research Center for Advanced Science and Technology, University of Tokyo
書誌事項
- タイトル別名
-
- Gas Nitriding of Magnesium — Titanium Alloys Fabricated by Bulk Mechanical Alloying
- Gas Nitriding of Magnesium — Titanium Alloys Fabricated by Bulk Mechanical Alloying
この論文をさがす
抄録
Mg–Ti alloys and pure Mg were successfully gas nitrided at 723 K for 129.6 ks under 0.1 MPa N2. Ti was selected as alloying element due to its high nitrogen affinity. Fine Ti particles in 10 \\micron range were homogeneously distributed in the alloys. Bulk Mechanical Alloying process was used to produce the sample having activated state of Mg, providing high diffusion path for nitrogen. Mg3N2 produced is not stable and reacts with moisture, resulting in fine powders of Mg(OH)2 on the surface and NH3(g) as by product.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (7), 1312-1316, 2001
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225116288
-
- NII論文ID
- 130004451571
- 30018849021
- 10006550775
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXmsFyrsLg%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 5889091
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可