Effect of Interface Behavior between Particles on Properties of Pure Al Powder Compacts by Spark Plasma Sintering
-
- Xie Guoqiang
- Graduate School of Science and Technology, Niigata University
-
- Ohashi Osamu
- Graduate School of Science and Technology, Niigata University
-
- Yoshioka Takayuki
- Graduate School of Science and Technology, Niigata University
-
- Song Minghui
- National Institute for Materials Science
-
- Mitsuishi Kazutaka
- National Institute for Materials Science
-
- Yasuda Hidehiro
- National Institute for Materials Science
-
- Furuya Kazuo
- National Institute for Materials Science
-
- Noda Tetsuji
- National Institute for Materials Science
この論文をさがす
抄録
Pure Al powder was sintered by spark plasma sintering (SPS) process at various sintering temperatures and loading pressures. The density, electrical resistivity, tensile properties and microstructure of powder compacts were investigated. The powder compacts with the similar properties as base aluminum metal was obtained at sintering temperature above 873 K, loading pressure above 23.5 MPa. For the powder compacts with the similar density but with the large difference in the electrical resistivity and tensile properties, the interfaces between Al powder particles were investigated using high resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray spectroscopy (EDS). Two types of interfaces, with metal/metal bonding and metal/oxide film layer/metal bonding, were observed in Al powder compacts. The properties of powder compacts were mainly subject to the behavior of oxide film between the powder particles.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (9), 1846-1849, 2001
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204245993344
-
- NII論文ID
- 130004451597
- 10006941205
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXotlCgsLc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 5923119
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可