高分子仕上塗材が鉄筋コンクリートの物理的寿命に及ぼす影響

DOI Web Site 参考文献27件
  • 福島 敏夫
    Department of Environmental Space Design, Faculty of Environmental Engineering, The University of Kitakyushu

書誌事項

タイトル別名
  • Influence of Polymeric Coating Materials on Physical Service Life of Reinforced Concrete
  • コウブンシ シアゲ トザイ ガ テッキン コンクリート ノ ブツリテキ ジュミョウ ニ オヨボス エイキョウ

この論文をさがす

抄録

Physical service life of steel reinforced concrete (RC) components and buildings in the ordinary atmospheric surroundings is reasonably determined by the time when the occurrence of crack and spalling of cover concrete makes serious damage to the daily safety as the results of the progress of neutralization of concrete and the accompanying corrosion of reinforcing steel. If we make effective use of polymeric coating materials, however, the physical service life can be prolonged by their suppressive effects against the progress of neutralization and corrosion. I propose the rational setting methods of physical service life of reinforced concrete treated with polymeric coating materials based upon the concept of equivalent thickness of cover concrete and also equivalent corrosion loss of crack occurrence.

収録刊行物

参考文献 (27)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ