シリカ配合およびカーボン配合ＳＢＲの摩擦機構に関する研究　第２報　　ぬれ面との摩擦

• 網野 直也

  横浜ゴム(株)

• 内山 吉隆

  金沢大学工学部

• 岩井 智昭

  金沢大学工学部

書誌事項

タイトル別名

• Studies on the Friction Mechanism of Silica-Filled and Carbon Black-Filled SBRs, Part 2. Friction on a Wet Surface
• シリカ ハイゴウ オヨビ カーボン ハイゴウ SBR ノ マサツ キコウ ニ カンスル ケンキュウ ダイ2ホウ ヌレ メン ト ノ マサツ
• Friction on a Wet Surface
• ぬれ面との摩擦

抄録

It is known that the hysteresis component of friction greatly contributes to the wet traction of tires, because the lubricant film prevents the tires from contacting the road. There are a lot of studies that have compared the wet skid resistance and the hysteresis loss of rubber. However the adhesion component of friction should also be evaluated.<br>In this paper, the friction forces are measured when rubbers are rubbed against the lubricated metal gauze. The variations of the friction force with the sliding speed are different from the hysteresis loss of the rubbers. At the low sliding speed region, the rubber specimens partially contact with the metal gauze and the contact area decreases with increasing sliding speed. At that time, the friction forces also include the adhesion component together with the hysteresis component.<br>The adhesion component of friction for rubbers rubbed against the wet metal gauze depends on the directly contacted area on to the metal gauze and shear strengths of the rubbers. Especially silica-filled SBRs have an effect to raise the adhesion component of friction at low sliding speed.

収録刊行物

• 日本ゴム協会誌

  日本ゴム協会誌 74 (11), 443-449, 2001

  一般社団法人 日本ゴム協会

キーワード

• Friction
• Adhesion
• Hysteresis
• Viscoelastic property
• Silica-filled SBR
• Carbon black-filled SBR
• Tribology

詳細情報

• CRID: 1390001206560628480
• NII論文ID: 10007268466
• NII書誌ID: AN00269207
• DOI: 10.2324/gomu.74.443
• COI: 1:CAS:528:DC%2BD2cXhtVejsb3F
• ISSN: 18840442
• ISSN: 0029022X
• NDL書誌ID: 5970648
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I5970648
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可