- A Study on the Measurement of Young's Modulus of Hot-Dip Zn Coated Steel by Laser Speckle Interferometry.
- レーザ スペックル カンショウホウ オ モチイタ ヨウユウ Znメッキ ショリ コウ ノ タテダンセイ ケイスウ ノ ケイソク
この論文をさがす
抄録
Laser speckle interferometry method can measure strain and displacement of material without contact. But, this method has a week point about the accuracy when applied to the rough surfaced object. Then, in this paper, laser speckle interferometry method was applied to measure the elastic properties of Hot-Dip Zn coated steel that has rough surface. The results are as follows.<br>1) Apparent Young's modulus of Hot-Dip Zn coated steel decreases with the increase of galvanized layer.<br>2) The Young's modulus of the (δ1+η) mixture layer and columnar layer, estimated by the compound rule and the multiple regression analysis, became 45.0GPa and 62.3GPa, respectively.<br>3) According to the above conclusions, the laser speckle interferometry method can be applied to measure the elastic properties of rough surfaced composite specimens.
収録刊行物
-
- 表面技術
-
表面技術 52 (7), 513-516, 2001
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679092604416
-
- NII論文ID
- 10007812398
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 5844552
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可