Relationship between Pre-sintering Conditions and Sintering behavior of Bi0.5(Na,K)0.5TiO3 Ceramics Textured by Reactive Templated Grain Growth Method.
-
- Tani Toshihiko
- Toyota Central Research and Development Laboratories, Inc.
-
- Fukuchi Eiichiro
- Keio University
-
- Kimura Toshio
- Keio University
この論文をさがす
抄録
The effects of pre-sintering conditions were investigated on the final density and texture of piezoelectric Bi0.5(Na, K)0.5TiO3 (BNKT) ceramics prepared by the reactive templated grain growth (RTGG) method. Bi4Ti3O12 (BiT) platelets were used as a reactive template for the fabrication of BNKT with a preferred <100> orientation. The application of cold isostatic pressing (CIP) after the in-situ formation of regular perovskite-type BNKT was effective to increase green density before sintering and thus to increase the final density. The CIP treatment after the completion of in-situ conversion from layered perovskite into regular perovskite, however, resulted in sintered ceramics with the lower degree of orientation. The CIP treatment after the partial in-situ formation of perovskite phase produced both dense and highly textured BNKT ceramics.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (3), 198-202, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308329472
-
- NII論文ID
- 10008007573
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD38XjvVWqt70%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 6126527
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可