Static Recrystallization and Induced Precipitation in a Low Nb Microalloyed Steel.
-
- Gómez M.
- Centro Nacional de Investigaciones Metalúrgicas (CENIM-CSIC)
-
- Medina S. F.
- Centro Nacional de Investigaciones Metalúrgicas (CENIM-CSIC)
-
- Quispe A.
- Centro Nacional de Investigaciones Metalúrgicas (CENIM-CSIC)
-
- Valles P.
- National Institute of Aerospace Technology, Spain
この論文をさがす
抄録
By simulation of hot rolling using torsion tests and subsequent graphic representation of mean flow stress (MFS) versusthe inverse of temperature for each pass, no-recrystallization temperature (Tnr) was determined for a low niobium microalloyed steel at different interpass times and two strains of 0.20 and 0.35. Recrystallized fraction (Xa) against time curves and RPTT diagrams were also determined for these two strains. This work has allowed evaluation of the influence of a very low Nb content on three aspects: Tnr, the residual stress accumulated in the austenite just before the γ→α transformation (Δσr), and recrystallization-precipitation interaction. It was found that when the strain applied was 0.2 and the interpass times were less than 30 s, the values of Tnr and Δσr were rather high. However, greater strains and interpass times brought about very small values of Tnr and Δσr. In addition to this, new aspects about the definition of Tnr are also discussed in this paper.
収録刊行物
-
- ISIJ International
-
ISIJ International 42 (4), 423-431, 2002
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206451130624
-
- NII論文ID
- 10008009024
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BD38XksVyrsbc%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可