ブルーレーザー対応型光ディスクにおける特性の改善

DOI Web Site 参考文献3件

書誌事項

タイトル別名
  • Improvement of Characteristics on Optical Disk at the Wavelength of Blue Laser.
  • ブルーレーザー タイオウガタ ヒカリディスク ニ オケル トクセイ ノ カイゼン

この論文をさがす

抄録

Thin films (of 50 nm thick) with a stacked structure (of 10150 layers) of In2O3 and ZnO have been deposited onto the glass and the polycarbonate substrates using the split target consisting of In2O3 and ZnO by a pulsed laser technique with an ArF excimer laser. A relation of the transmittance change ΔT at the wavelength of 400 nm between the annealed state (480°C × 20 min) and the as-deposited state versus the number of layers for the structure fabricated at the trace ratio of In2O3 : ZnO = 1 : 1 was obtained. The structure with 20 layers showed the maximal value of ΔT. SEM observation revealed that the surfaces of these films were enough smooth to use in static or revolution tests for'write'. AFM observation showed that surface roughness of the as-deposited state and the annealed state were Ra of 0.76 nm and Ra of 2.25 nm respectively. A peak power dependence of CNR of 3T signal (λ = 406 nm, NA = 0.65) at a linear velocity of 5 m/s and a read power of 0.6 mW was measured for the disk samples with 60-layers fabricated for the revolution tests. That the write power of less than 3 mW was required and maximal value of CNR = 67 dB was obtained. The values of CNR could be improved by optimizing the number of layers and the film compositions.

収録刊行物

  • 真空

    真空 45 (3), 247-250, 2002

    一般社団法人 日本真空学会

参考文献 (3)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ