- Iorio Luana E.
- GE Corporate Research and Development
-
- Garrison, Jr. Warren M.
- Department of Materials Science and Engineering, Carnegie Mellon University
この論文をさがす
抄録
A titanium carbosulfide solubility product of log [Ti][C]0.5[S]0.5 = -14 646/T15.51 and a Gibbs free energy of formation for titanium carbosulfide of Δ°GTi<sub>4C2S2</sub> = -1 121.9+0.196 T kJ/mol were calculated from dissolution temperature experiments using a series of titanium-modified secondary hardening ultra-high strength steels.<BR>The presence of other precipitates such as TiN, TiC and TiS could be neglected for this class of steels. The effect of the alloying additions on the activity of carbon and hence on the dissolution temperature of titanium carbosulfide was also found to not be significant for these steels. The experimentally determined solubility product and Gibbs free energy of formation are compared with previously published data for titanium carbosulfide.
収録刊行物
-
- ISIJ International
-
ISIJ International 42 (5), 545-550, 2002
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206453988736
-
- NII論文ID
- 10008223117
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BD38XltVygtrw%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可