Dy-Ba-Cu-O系バルク超伝導材料の捕捉磁場特性に及ぼすDy<SUB>2</SUB>BaCuO<SUB>5</SUB>添加量の影響
書誌事項
- タイトル別名
-
- Effect of Dy<SUB>2</SUB>BaCuO<SUB>5</SUB> Addition on Trapped Magnetic Fields in Dy-Ba-Cu-O Bulk Superconductors
- Dy-Ba-Cu-O系バルク超伝導材料の捕捉磁場特性に及ぼすDy2BaCuO5添加量の影響
- Dy Ba Cu Oケイ バルク チョウデンドウ ザイリョウ ノ ホソク ジバ トクセイ ニ オヨボス Dy2BaCuO5 テンカリョウ ノ エイキョウ
この論文をさがす
抄録
The effect of Dy2BaCuO5 (Dy211) contents on the field trapping properties of Ag-added DyBa2Cu3Oy (Dy123) single domain bulk has been investigated. The Dy-Ba-Cu-O/Ag bulks 32 mm in diameter with different Dy211 contents were fabricated in air with the top-seeded melt-growth method using NdBa2Cu3O7 seed crystal. The trapped magnetic fields were measured as a function of external field and compared with the Jc-B properties, in that a similar field dependency was observed. In the case of the Dy123 bulk with excess 5 mol% Dy211, the peak was found at around 0.5-1.5 T of external field in the trapped field measurement at 77 K. The value of trapped field was 1.2 T at the peak field. This result reflects the secondary peak effect in Jc-B properties of the bulk samples. On the other hand, the trapped field of Dy123 bulk with excess 40 mol% of Dy211 exhibited 1.4 T when the applied field was removed. This value monotonously decreased with increasing external field, since this sample showed no secondary peak effect in Jc-B properties.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 66 (4), 315-319, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206492050304
-
- NII論文ID
- 130007342480
- 10008832583
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 6151557
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可