SUS316L高ひずみ付加PMプロセス材の熱処理による組織変化  [in Japanese] Change in Structure by Heat Treatment of SUS316L HS-PM Process Material  [in Japanese]

Access this Article

Search this Article

Author(s)

Abstract

The high strain powder metallurgy (HS-PM) process was applied to an SUS316L gas atomized powder by 360ks mechanical milling (MM) with a planetary ball mill under an Ar atmosphere. The MM powder was annealed at 1073 K, 1173 K, 1273 K. Each structure was investigated using XRD and TEM/EDS. It was confirmed that as-MM powder consisted of an ultra fine (α+γ) microduplex structure. It was supposed that the a phase was formed as the HS-PM process by increasing free energy of the austenitic phase. Fine grain structure with its grain size of 2.3μm composed of fine carbides and γ phase was obtained when MM powder was annealed at 1073 K for 3.6 ks. It was also confirmed that these fine carbides restrain the grain growth. But at 1173 K and 1273 K, the fine carbides were not seen, so that grain size increased drastically.

Journal

  • Journal of the Japan Society of Powder and Powder Metallurgy

    Journal of the Japan Society of Powder and Powder Metallurgy 49(6), 479-485, 2002-06-15

    Japan Society of Powder and Powder Metallurgy

References:  15

Codes

  • NII Article ID (NAID)
    10008833448
  • NII NACSIS-CAT ID (NCID)
    AN00222724
  • Text Lang
    JPN
  • Article Type
    ART
  • ISSN
    05328799
  • NDL Article ID
    6190473
  • NDL Source Classification
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL Call No.
    Z17-274
  • Data Source
    CJP  NDL  J-STAGE 
Page Top