- Influence of Milling Treatment by Mechanofusion Apparatus on Magnetic Properties of Sr-Ferrite Powder and the Compacts.
- Sr フェライトフン ト ソノ セイケイタイ ノ ジキ トクセイ ニ オヨボス メカノフュージョン ショリ ノ エイキョウ
この論文をさがす
抄録
To investigate effects of shear stress and shear strain on the magnetic properties of Sr-ferrite powder, the powder was milled by a mechanofusion (MF) apparatus, and its magnetic characteristics were studied. Coercive force of the MF-milled powder was decreased with milling time, and it reached the constant value of 140 kA⋅m-1 as milling time was longer than 30 min. Reduction of the coercive force of the milled powder was found to slightly improve degree of powder particle alignment under applied magnetic fields. M-type ferrite phase of the original Sr-ferrite powder remains unchanged after the MF-milling treatment. The mean particle size of the powder was increased by a MF-milling treatment longer than 30 min due to aggregation of the powders. As a result, the optimum MF-milling time was in the range from 15 min to 30 min under the experimental conditions of this study.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (8), 744-748, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206309157248
-
- NII論文ID
- 10009579895
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6273595
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可