Fabrication and Mechanical Property of Lotus-type Porous Magnesium
-
- Ikeda Teruyuki
- The Institute of Scientific and Industrial Research, Osaka University
-
- Nakajima Hideo
- The Institute of Scientific and Industrial Research, Osaka University
Bibliographic Information
- Other Title
-
- ロータス型ポーラスマグネシウムの作製と機械的性質
- 技術報告 ロータス型ポーラスマグネシウムの作製と機械的性質
- ギジュツ ホウコク ロータスガタ ポーラス マグネシウム ノ サクセイ ト キカイテキ セイシツ
Search this article
Abstract
Lotus-type porous magnesium, in which countless small pores elongated in the solidification direction are dispersed, was fabricated by unidirectional solidification under hydrogen atmosphere. Ingots with various sets of porosities and averaged pore diameter can be obtained by controlling the pressure of hydrogen atmosphere. In the present experiments, porous magnesium ingots with porosities and averaged pore diameters in the range of 0~50% and 60~800μm were fabricated. These materials are very light weight ; porous magnesium with 50% porosity has a density of 0.87g/cm3 and floats in water. The anisotropy in tensile strength of porous magnesium was observed and it was found that the tensile strength in the direction parallel to the pores is higher than that perpendicular.
Journal
-
- Journal of Japan Foundry Engineering Society
-
Journal of Japan Foundry Engineering Society 74 (12), 812-816, 2002
Japan Foundry Engineering Society
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681487366912
-
- NII Article ID
- 10010085367
-
- NII Book ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL BIB ID
- 6381453
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed