Electrochemical Characteristics of <I>Niiro</I>-colored Cupper Colored by Japanese Traditional Craft-technique
-
- Kitada Masahiro
- Tokyo National University of Fine Arts and Music
-
- Kirino Fumiyoshi
- Tokyo National University of Fine Arts and Music
-
- Tsuru Tooru
- Tokyo Institute of Technology
-
- Sugimoto Katsuhisa
- Tohoku University
-
- Matsushima Tomohide
- Tokyo National University of Fine Arts and Music
Bibliographic Information
- Other Title
-
- 伝統技法で煮色着色した銅の電気化学特性
- デントウ ギホウ デ ニショク チャクショク シタ ドウ ノ デンキ カガク トクセイ
Search this article
Abstract
The electrochemical characteristics and corrosion behavior of Niiro-colored Cu, colored by a traditional Japanese craft technique, have been investigated. The specimens are colored in a solution containing CuSO4, artificial malachite powder and alum. The oxidation potential of Niiro-colored Cu is higher than that of untreated Cu, indicating that the corrosion resistance of Niiro-colored Cu is higher than that of untreated Cu. Although the reaction electron number of untreated Cu is approximately two, the number of Niiro-colored Cu is unity in 2-8 pH solutions. The Niiro-colored Cu surface consists of double layers chemically. The thin upper layer is a copper(II) oxide such as CuO and the underlayer is a copper(I) oxide such as Cu2O. Niiro-colored Cu shows good corrosion resistance when the specimens are exposed at 353 K in 90%RH atmosphere. The oxidation potential of Niiro-colored Cu in a solution containing Cl− of 8.3 pH is higher than that of untreated Cu.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 66 (12), 1356-1361, 2002
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681467893120
-
- NII Article ID
- 130007341779
- 10010601166
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
- http://id.crossref.org/issn/00214426
-
- NDL BIB ID
- 6409290
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed