Gas-Desorption Properties of Inner Coating Materials Used for Cathode-Ray Tube-Effect of Water Glass Component of Inner Coating Material on Gas Desorption-
-
- HASHIBA Masao
- Department of Nuclear Engineering, Hokkaido University
-
- HIROHATA Yuko
- Department of Nuclear Engineering, Hokkaido University
-
- HINO Tomoaki
- Department of Nuclear Engineering, Hokkaido University
-
- YAMADA Hidekazu
- Chemical Products Div., Hitachi Powdered Metals Co., Ltd.
-
- KOIDE Akio
- Chemical Products Div., Hitachi Powdered Metals Co., Ltd.
-
- KUBOTA Yoshihiro
- Chemical Products Div., Hitachi Powdered Metals Co., Ltd.
書誌事項
- タイトル別名
-
- Effect of Water Glass Component of Inner Coating Material on Gas Desorption
この論文をさがす
抄録
For two types of inner coating materials with different component of water glass, the gas desorption properties were measured by using thermal desorption spectroscopy.<BR>The major outgassing species during the heating up to 773 K were CO2 and H2O in both types. In the thermal desorption spectra of CO2 and H2O, a large desorption peak was observed at approximately 400 K. The total desorption amount of CO2 and H2O for the (A + B) type with the water glass, (K2O + Li2O) ·3.8SiO2·4H2O, was approximately a half of that of the A type with the water glass, K2O·3.8SiO2·4H2O. The (A + B) type can reduce both the baking temperature and the pumping time in the manufacturing process of cathod ray tube, compared to the A type.
収録刊行物
-
- 真空
-
真空 46 (7), 539-541, 2003
一般社団法人 日本真空学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204063868416
-
- NII論文ID
- 10011611141
-
- NII書誌ID
- AN00119871
-
- ISSN
- 18809413
- 05598516
-
- NDL書誌ID
- 6661499
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可