Dielectric property of single crystalline BaTi2O5 prepared by a floating zone method
-
- Akashi Takaya
- Institute for Materials Research, Tohoku University
-
- Iwata Hiroaki
- Institute for Materials Research, Tohoku University
-
- Goto Takashi
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Dielectric Property of Single Crystalline BaTi<SUB>2</SUB>O<SUB>5</SUB> Prepared by a Floating Zone Method
この論文をさがす
抄録
Single crystalline BaTi2O5 was prepared by a floating zone method. The permittivity of single crystalline BaTi2O5 perpendicular to a (010) plane showed the maximum value of 20500 at 748 K obeying the Curie-Weiss law at higher temperatures. The permittivity perpendicular to (100) and (001) planes were 140 and 70, respectively almost independent of temperature. A transition temperature measured by a dilatometer was in agreement with a Curie temperature. The relationship between polarization and electrical field perpendicular to the (010) plane showed ferroelectric hysteresis. No hysteresis was observed in the direction perpendicular to (100) and (001) planes. The electrical conductivity perpendicular to the (010) was larger than those of (100) and (001) planes. The activation energy of electrical conductivity was 147 to 180 kJ mol−1 independent of directions.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (8), 1644-1646, 2003
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222768768
-
- NII論文ID
- 130004452233
- 10011914232
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXnsFylurg%3D
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/52319
-
- NDL書誌ID
- 6652738
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可