Microstructures and Fracture Characteristic of Si3N4-O'SiAlON Composites using Waste-Si-Sludge
-
- Lee Byong-Taek
- Division of Advanced Materials Engineering, Kongju National University
-
- Jeong Ha-Guk
- Institute for Materials Research, Tohoku University
-
- Hiraga Kenji
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Microstructures and Fracture Characteristic of Si<SUB>3</SUB>N<SUB>4</SUB>-O’SiAlON Composites using Waste-Si-Sludge
- Microstructures and Fracture Characteristic of Si<SUB>3</SUB>N<SUB>4</SUB>-O’SiAlON Composites using Waste-Si-Sludge
この論文をさがす
抄録
Si3N4–O’SiAlON composites using waste-Si-sludge was fabricated by gas-pressure-sintering (GPS) process at 1950°C for 3.5 h. The percent nitridation of waste Si compacts showed a lower value than that of using commercial Si powders caused by the high contents of oxygen in the waste Si particles. Some amounts of Si2N2O and Y2Si2O7 phases were also detected in the reaction-bonded Si3N4 (RBSN) although main components were α-Si3N4, β-Si3N4 and residual Si phases. In the post-sintered body by GPS, no residual Si, α-Si3N4, Si2N2O and Y2Si2O7 phases were detected except the β-Si3N4 and O’SiAlON. The grain growth of rod-like Si3N4 grains was inhibited by the dispersion of fine O’-SiAlON particles. The fracture toughness and strength of Si3N4–O’SiAlON composites were 5.6 MPa·m1⁄2 and 456 MPa, respectively.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (1), 19-23, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222792576
-
- NII論文ID
- 130004451642
- 10012320341
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XitlSrtLo%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6051185
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可