- Mano S.
- Department of Materials Science, Faculty of Engineering, Kitami Institute of Technology
-
- Hashi K.
- Department of Materials Science, Faculty of Engineering, Kitami Institute of Technology
-
- Ishikawa K.
- Department of Materials Science, Faculty of Engineering, Kitami Institute of Technology
-
- Aoki K.
- Department of Materials Science, Faculty of Engineering, Kitami Institute of Technology
書誌事項
- タイトル別名
-
- Hydrogen Absorption and Desorption Properties of Ti<SUB>3</SUB>Al-Ni Alloys
この論文をさがす
抄録
Structures of as-cast and homogenized Ti75−xAl25Nix alloys before and after hydrogenation, the hydrogen content and the hydrogen desorption temperature of the hydrogenated Ti75−xAl25Nix alloys were investigated by a powder X-ray diffractometer (XRD) and a hydrogen analyzer. The hydrogen content of these alloys decreased with increasing Ni content, and was almost independent of the hydrogenation temperature and the structure of the alloys, but 50% hydrogen desorption temperature, Td, varied widely with them. The formation of amorphous phases raised Td. On the contrary, a drop in Td was achieved by hydrogenation of a mixture alloy of the D019 and C14 Laves phases.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (3), 421-423, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679223368960
-
- NII論文ID
- 130004451811
- 10012321476
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XjsFGrsr0%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6110975
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可