Phase Transformation Behavior and Shape Memory Characteristics of Ti-Ni-Cu-Mo Alloys
-
- Nam Tae-Hyun
- Division of Materials Engineering, Gyeongsang National University & ERI
-
- Noh Jung-Phil
- Division of Materials Engineering, Gyeongsang National University & ERI
-
- Hur Shin-Goo
- Biosmart Ltd
-
- Kim Ji-Soon
- Department of Materials Science and Engineering, Ulsan University
-
- Kang Seung-Baik
- Seoul Municipal Boramae Hospital
この論文をさがす
抄録
Phase transformation behavior, the shape memory characteristics and the superelasticity of Ti–Ni–Cu–Mo alloys have been investigated by means of electrical resistivity measurements, X-ray diffraction, thermal cycling tests under constant load and tensile tests. A fully annealed Ti–44.7Ni–5Cu–0.3Mo alloy transformed in two-stage, i.e., the B2-B19-B19′ on cooling and the B19′-B19-B2 on heating. Fully annealed Ti–39.7Ni–10Cu–0.3Mo, Ti–34.7Ni–15Cu–0.3Mo and Ti–29.7Ni–20Cu–0.3Mo alloys transformed in one-stage on, i.e., from the B2 to the B19 on cooling and from the B19 to B2 on heating. The maximum recoverable elongation deceased from 6.0 to 2.4% with increasing Cu-content from 5 to 20 at%. Transformation hysteresis associated with the B2-B19 transformation decreased from 11 to 5 K with increasing Cu-content from 5 to 20 at%. Substitution of Mo for Ni in Ti–Ni–Cu alloys improved the superelasticity.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (5), 802-808, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204246957056
-
- NII論文ID
- 10012322735
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xlt1ensLc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6179334
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可