Preparation of WC-WB-W<SUB>2</SUB>B Composites from B<SUB>4</SUB>C-W-WC Powders and their Mechanical Properties
-
- Sugiyama Shigeaki
- Akita Prefectural Industrial Technology Center
-
- Taimatsu Hitoshi
- Department of Materials Science and Engineering, Faculty of Engineering and Resource Science,Akita University
Bibliographic Information
- Other Title
-
- Preparation of WC-WB-W2B Composites from B4C-W-WC Powders and their Mechanical Properties
Search this article
Abstract
Sintered composites of WC–WB–W2B were prepared from B4C–W–WC powders using a reactive energization hot-pressing technique that initiated a solid state reaction between B4C and W. Below a WC mole fraction of 0.769 in the starting powder, WB and WC were formed according to the reaction B4C+5W+xWC=WB+(1+x)WC, while WB, W2B, and WC were produced above a mole fraction of 0.854. Densely sintered bodies were not obtained for pure WC. Composites of WC–WB–W2B obtained at WC mole fractions between 0.854 and 0.956 were fully consolidated, having high Young’s modulus and Vickers hardness values, and a fracture toughness which were comparable to those of WC.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (5), 1197-1201, 2002
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204247822080
-
- NII Article ID
- 10012323818
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xlt1enu7Y%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 6180576
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed