Effect of Nb on Microstructural Characteristics of Ti-Nb-Ta-Zr Alloy for Biomedical Applications

この論文にアクセスする

この論文をさがす

著者

抄録

The effects of several commonly used heat treatment schemes on the microstructures of two Ti–Nb–Ta–Zr alloys aimed at biomedical applications were studied in this work using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The specimens were water quenched from 790°C and then aged at temperatures between 300°C and 600°C. The experimental results showed that α and ω phase precipitated from the metastable β matrix in Ti–29Nb–13Ta–4.6Zr alloy during isothermal ageing. But for Ti–39Nb–13Ta–4.6Zr, the precipitation reaction was more sluggish than that in Ti–29Nb–13Ta–4.6Zr because of high amount of β stabilizing elements in the former alloy. As a result the α phase was unable to precipitate during short time ageing treatment. After longer time (12 days) ageing treatment at 500°C or 400°C, recognizable α precipitates were observed in the aged samples. It is concluded that Ti–29Nb–13Ta–4.6Zr can be heat treated to obtain different microstructures and is better than Ti–39Nb–13Ta–4.6Zr in terms of age hardenability.

収録刊行物

  • Materials transactions

    Materials transactions 43(12), 2964-2969, 2002-12-01

    日本金属学会

参考文献:  29件中 1-29件 を表示

被引用文献:  3件中 1-3件 を表示

各種コード

  • NII論文ID(NAID)
    10012328706
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    6394951
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  CJP引用  NDL  IR  J-STAGE 
ページトップへ