The Effect of Ta Content on Phase Constitution and Aging Behavior of Ti-Ta Binary Alloys
-
- Ikeda Masahiko
- Department of Materials Science and Engineering, Faculty of Engineering, Kansai University
-
- Komatsu Shin-ya
- Department of Materials Science and Engineering, Faculty of Engineering, Kansai University
-
- Nakamura Yuichiro
- Graduate Student of Kansai University
書誌事項
- タイトル別名
-
- Effect of Ta Content on Phase Constitution and Aging Behavior of Ti Ta Binary Alloys
この論文をさがす
抄録
Using Ti–Ta alloy to which Ta was added systematically, i.e. Ti–5 mass%Ta, 10 mass%Ta, 20 mass%Ta, 30 mass%Ta, 40 mass%Ta and 50 mass%Ta alloys, the effect of Ta concentration on phase constitution in the solution treated and quenched state and aging behavior is studied by electrical resistivity and Vickers hardness measurements and X-ray diffactometry. All alloys were solution treated at 1173 K for 3.6 ks and then quenched into ice water (STQ). STQed specimens were isochronally heat treated from 323 to 1173 K . STQed specimens of Ti–50 mass%Ta alloy were isothermally aging at five different temperatures, 573 K, 623 K, 673 K, 723 K and 773 K. In the solution treated and quenched state, only reflections of hexagonal martensite, α′ were obserevd by XRD in Ti–5Ta to 30Ta alloys, whereas only orthorhombic martensite, α′′, was identified by XRD in Ti–40Ta and 50Ta alloys. α′′ in Ti–50Ta alloy is reversely transformed into β upon isochronal heat treatment: the starting temperature is situated at a temperature between 623 K and 673 K . Isothermal aging of this alloy shows that α′′ directly decomposes to α and β phases without reverse transformation of α′′ at 573 K and 623 K aging. On isothermal aging above 673 K, α′′ reversely transforms into β and then isothermal ω phase precipitates in the reversed β.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (12), 2984-2990, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222271488
-
- NII論文ID
- 10012328763
- 30018850289
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXhtF2nu7w%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6394987
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可