Influence of Low Oxygen Contents and Alloy Refinement on the Glass Forming Ability of Zr_<52.5>Cu_<17.9>Ni_<14.6>Al_<10>Ti_5

この論文にアクセスする

この論文をさがす

著者

抄録

The effect of additions of C, Si, Ca, Sc and La at levels of 0.1, 0.3 and 1.0 atomic percent on the glass forming ability of the alloy Zr<SUB>52.5</SUB>Cu<SUB>17.9</SUB>Ni<SUB>14.6</SUB>Al<SUB>10</SUB>Ti<SUB>5</SUB> has been investigated by means of metallography, X-ray diffraction and oxygen analysis using wedge shaped castings. In the original alloy, a very marked influence of oxygen on the glass forming ability is observed even at low concentrations. Low amounts of additional elements were found to influence the glass forming ability significantly. Adding Sc to alloys containing 100–120 ppm oxygen increases the glass forming ability from 4.5 to 10 mm in terms of amorphous ingot thickness. These results were confirmed with additional samples, and best glass forming ability was found with additions of 0.03% to 0.06%Sc. The maximum amorphous thickness in the wedges as measured by metallography correlates within an accuracy of about 1 mm with that measured by X-ray diffraction over a wide range of modified alloys. A possible mechanism for the enhancement of glass formation through these dopants, and reasons for their effectiveness over only a limited concentration range, are discussed using results from differential scanning calorimetry and differential thermal analysis on a series of samples with different Sc concentrations.

収録刊行物

  • Materials transactions

    Materials transactions 43(12), 3206-3210, 2002-12-01

    公益社団法人 日本金属学会

参考文献:  18件中 1-18件 を表示

各種コード

  • NII論文ID(NAID)
    10012329555
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    6395577
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ