AE法を用いた低温衝撃をうけるGFRP板の損傷解析 Damage Analysis of CFRP Plates Exposed to Cryogenic Shock by AE Monitoring

この論文にアクセスする

この論文をさがす

著者

抄録

In order to investigate fracture modes and timing for two types of CFRP plates during cryogenic shock testing, Acoustic Emission (AE) monitoring was conducted. No damage was observed for the specimen that made of heat-resistant matrix, however, thirty-nine matrix cracks were observed for the other specimen. Several cracks were observed even at the location where temperature differences on both surfaces were small. The AE signals were classified into three types by waveform characteristics according to the damage behavior. After that, three fracture modes of matrix crack, delamination and transverse cracks were simulated by pulse-laser irradiation to the CFRP plate and the detected AE signals were compared to estimate those obtained at cryogenic shock testing. The number of the AE signals linearly increased untill the LN<SUB>2</SUB> disappeared from the cooling cell. Then, we conducted the vertical immersion test to examine the influence of cooling temperature to the damage occurrences. At temperatures lower than 228K, matrix cracks initiated at the specimen surface. At 213K, large number of AE signals due to matrix crack and few number of AE signals due to delamination and transverse crack were observed. At 77K, large number of AE signals caused by three types of fractures was detected.

収録刊行物

  • 日本複合材料学会誌 = Journal of the Japan Society for Composite Materials

    日本複合材料学会誌 = Journal of the Japan Society for Composite Materials 29(6), 226-233, 2003-11-15

    JAPAN SOCIETY FOR COMPOSITE MATERIALS

参考文献:  11件中 1-11件 を表示

各種コード

  • NII論文ID(NAID)
    10012517573
  • NII書誌ID(NCID)
    AN00196748
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03852563
  • NDL 記事登録ID
    6764803
  • NDL 雑誌分類
    ZM16(科学技術--科学技術一般--工業材料・材料試験)
  • NDL 請求記号
    Z14-655
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ